A light-responsive wound dressing hydrogel: Gelatin based self-healing interpenetrated network with metal-ligand...

Interpenetrated network (IPN) hydrogels with desired mechanical properties were prepared based on gelatin. A copolymer of dimethyl aminoethyl methacrylate (DMAEMA) with 2-Acrylamido-2-methylpropane sulfonic acid (AMPS) in gelatin was chemically cross-linked with methylene bis acrylamide (MBA) to form a semi-IPN hydrogel. Also, IPN hydrogel is fabricated from the AMPS-co-DMAEMA and gelatin in the presence of ferric ions with both chemical and physical cross-linkers. According to the compression test, the metal-ligand interaction has a remarkable impact on the mechanical strength of hydrogel. Ferric ions caused a decrease in the pores size confirmed by the SEM images of hydrogels, resulting in preserving its mechanical stability during the swelling test due to a more robust structure of hydrogel. Ferric to ferrous ions reduction is observed under visible light irradiation, which results in a light-sensitive hydrogel with a higher rate of biodegradation compared to semi-IPN hydrogels. MTT assay results implied that the synthesized hydrogels are non-toxic for the L-929 cell line. Also, for more detailed investigations, histological studies are conducted as in vivo tests. With regards to the improvements of mechanical properties harnessed in IPN hydrogels by ferric ions along with the extraordinary self-healing capability, IPNs would be considered an appropriate option for tissue engineering.