Rheological Characterization and Printability of Sodium Alginate-Gelatin Hydrogel for 3D Cultures and Bioprinting

The development of biocompatible hydrogels for 3D bioprinting is essential for creating functional tissue models and advancing preclinical drug testing. This study investigates the formulation, printability, mechanical properties, and biocompatibility of a novel Alg-Gel hydrogel blend (alginate and gelatin) for use in extrusion-based 3D bioprinting. A range of hydrogel compositions were evaluated for their rheological behavior, including shear-thinning properties, storage modulus, and compressive modulus, which are crucial for maintaining structural integrity during printing and supporting cell viability. The printability assessment of the 7% alginate-8% gelatin hydrogel demonstrated that the 27T tapered needle achieved the highest normalized Printability Index (POI_normalized = 1), offering the narrowest strand width (0.56 ± 0.02 mm) and the highest printing accuracy (97.2%) at the lowest printing pressure (30 psi). In contrast, the 30R needle, with the smallest inner diameter (0.152 mm) and highest printing pressure (80 psi), resulted in the widest strand width (0.70 ± 0.01 mm) and the lowest accuracy (88.8%), resulting in a POI_normalized of 0.274. The 30T and 27R needles demonstrated moderate performance, with POI_normalized values of 0.758 and 0.558, respectively. The optimized 7% alginate and 8% gelatin blend demonstrated favorable printability, mechanical strength, and cell compatibility with MDA-MB-213 breast cancer cells, exhibiting high cell proliferation rates and minimal cytotoxicity over a 2-week culture period. This formulation offers a balanced approach, providing sufficient viscosity for precision printing while minimizing shear stress to preserve cell health. This work lays the groundwork for future advancements in bioprinted cancer models, contributing to the development of more effective tools for drug screening and personalized medicine.