Electrospray deposition of polymer thin films for organic light-emitting diodes

Electrospray process was developed for organic layer deposition onto polymer organic light-emitting diode [PLED] devices in this work. An electrospray can be used to produce nanometer-scale thin films by electric repulsion of microscale fine droplets. PLED devices made by an electrospray process were compared with spin-coated ones. The PLED device fabricated by the electrospray process showed maximum current efficiency of 24 cd/A, which was comparable with that of the spin-coating process. The electrospray process required a higher concentration of hole and electron transport materials in the inks than spin-coating processes to achieve PLED maximum performance. Photoluminescence [PL] at 407 nm was observed using electrosprayed poly(N-vinyl carbazole) films, whereas a peak at 410 nm was observed with the spin-coated ones. Similar difference in peak position was observed between aromatic and nonaromatic solvents in the spin-coating process. PLED devices made by the electrospray process showed lower current density than that of spin-coated ones. The PL peak shift and reduced current of electrosprayed films can therefore be attributed to the conformation of the polymer.